Our company is bracketed with reputed Manufacturers & Suppliers of Quick Drying Paints in Pune, Maharashtra, India. We provide 100% pure and superior grade Quick Drying Paints made from quality raw material. We make available Quick Drying Paints in a variety of grades and offer them at economical prices. Buyers interested in buying Quick Drying Paints in bulk can contact us.

Scope : A quick drying primer/Paints for use on structural steel. Provides a hard drying, Tough, formulated with rust inhibitors to resist corrosion on any metal surface, flows on smooth & covers completely with one easy to apply coat.

  • Recommended for use on bridges, cranes, towers, equipment, tanks etc.
  • Easy to apply.
  • Handlable within 30 minutes.
  • Recoatable when surface must be tack free.     

Yes! I am interested

Product Data : (PAINTS)

Type Single Pack
Composition Modified quick drying alkyd medium with suitably pigmented as per required shade.
Viscosity (Ford Cup B4) 70±10 Seconds
Specific Gravity 1.05±0.05
Application Brush/Roller/ Conventional Spray Gun
Recommended DFT 25±5µ per coat
Theoretical Spreading Rate 6-7 Sq. Mtr. / Liter
Drying Time
  • Surface Dry-10-15 min
  • Tack Free- 1-2 hours
  • Hard Dry-over night
Over coating interval Min: Overnight
Max: 2 Days
Flash Point Above 40ËC
Colour As per IS & RAL K5 Shade cards
Packing 4,10 & 20 Liters
Thinner Pragati make Q.D Thinner
Finish Smooth & Matt/ Semi Glossy/Glossy

 After complete curing, the following tests should be carried :

Examine Test Specification Result
Adhesion Test After 24 hrs. ( No lifting of film form) Pass
Scratch Hardness Test 1000-1500 gm. Pass
Flexibility To pass ¼ inch mandrel Pass
Salt Spray 100-160 Hrs. Pass
Humidity Test 140 hrs. No blistering / rusting & no loss of adhesion Pass
Resistance to Grease For 48 hrs. at R.T.No blistering. No deterioration of hardness, No failure of adhesion Pass

Resistance Guide :

Chemical Resistance
Exposures Splash & Spillage Mild Fumes/Outdoor Resistance
Acid N/R N/R Poor Poor
Alkalis N/R N/R Poor Fair
Solvents Fair Fair Fair Fair
Salt Good Good Good Good
Water Good Very Good Good Good


Temperature Resistance

  • Continuous- 90Ë
  • Intermittent- 120ËC

Weatherability : Good
Flexibility :  Good
Abrasion Resistance : Moderate


Storage Life : Up to 6 month in intact condition or sealed the containers are kept under cover in a dry place under normal temperature conditions.


Surface Preparation :
Steel : remove grease, oil & other contaminants preferably by using degreasing solvent. Blast clean to a minimum of Sa2 ½ Swedish std. SIS 05 5900. For severe corrosion, blast to Sa 3 with a surface profile not exceeding 65 microns.
If blasting is not practical, make full use of mechanical tools along with manual chipping & wire brushing to remove loose rust & scale to St. 2 Swedish std. SIS 05 5900. Excessive burning of steel is to be avoided. Thoroughly dust down all surfaces. Best results can be achieved if the manually cleaned surface is primed with protectomastic- self-priming surface tolerant coating; otherwise, treatment with metal conditioning solution will also produce satisfactory results.
The surface should be clean & dry before application of primer coat.


Application :

  • Mix the contents thoroughly before & during use.
  • Apply with suitable thinner for the recommended dry film thickness.
  • Brush / Roller: add up to 5% thinner if required during application.
  • Conventional spray: add up to 15-20% thinner depending on conditions. Use only standard equipment at an atomizing pressure of 3.5-4.9 Kg/cm2.


Note :

  • Do not apply when temperature falls below 10ËC or rises above 50ËC & when relative humidity rises above 90%. Do not apply during rain Fog or mist.
  • Brushes & Roller should be cleaned with thinner otherwise, equipment is liable to be damaged.
  • Primed steel work should not be exposed with one coat for a long period.