Pragati Paints & Allied Products


Quick Drying Primers


Image 01 Image 02

We are ranked among renowned Manufacturers & Suppliers of Quick Drying Primers in Pune, Maharashtra, India. Made from premium raw materials and using advanced machines, our Quick Drying Primers are easy to dry, reliable and durable. Our company offers Quick Drying Primers as per requirements in a variety of grades. Buyers can purchase Quick Drying Primers from us at competitive prices.

Scope : A quick drying primer/Paints for use on structural steel. Provides a hard drying, Tough, formulated with rust inhibitors to resist corrosion on any metal surface, flows on smooth & covers completely with one easy to apply coat.

  • Recommended for use on bridges, cranes, towers, equipment, tanks etc.
  • Easy to apply.
  • Handlable within 30 minutes.
  • Recoatable when surface must be tack free.

Features

QUICK DRYING / AIR DRYING / FAST DRYING ENAMEL BASE PAINT RED / GREY

Additional Information

Min. Order Quantity 4
Packaging Details 4 / 10/ 20 / 200 LITERS


Product Data : (PRIMERS)

Type Single Pack
Composition Modified quick drying alkyd medium with suitably pigmented
Viscosity (Ford Cup B4) 90±10 Seconds
Specific Gravity 1.25±0.05
Application Brush/Roller/ Conventional Spray Gun
Recommended DFT 30±5µ per coat
Theoretical Spreading Rate 5-6 Sq. Mtr. / Liter
Drying Time
  • Surface Dry-10-15 min
  • Tack Free- 1-2 hours
  • Hard Dry-over night
Over coating interval Min: Overnight
Max: 2 Days
Flash Point Above 40˚C
Colour Grey, Red oxide
Packing 4,10 & 20 Liters
Thinner Pragati make Q.D Thinner
Finish Grey-Smooth & Matt
Red oxide- Smooth & Matt/Glossy

Resistance Guide :

Chemical Resistance
Exposures Splash & Spillage Mild Fumes/Outdoor Resistance
  PRIMERS PAINTS PRIMERS PAINTS
Acid N/R N/R Poor Poor
Alkalis N/R N/R Poor Fair
Solvents Fair Fair Fair Fair
Salt Good Good Good Good
Water Good Very Good Good Good

Temperature :

  • Continuous- 90˚ C
  • Intermittent- 120˚ C

Weatherability : Good
Flexibility :  Good
Abrasion Resistance : Moderate

 

Storage Life : Up to 6 month in intact condition or sealed the containers are kept under cover in a dry place under normal temperature conditions.

 

Surface Preparation :
Steel : remove grease, oil & other contaminants preferably by using degreasing solvent. Blast clean to a minimum of Sa2 ½ Swedish std. SIS 05 5900. For severe corrosion, blast to Sa 3 with a surface profile not exceeding 65 microns.
If blasting is not practical, make full use of mechanical tools along with manual chipping & wire brushing to remove loose rust & scale to st. 2 Swedish std. SIS 05 5900. Excessive burning of steel is to be avoided. Thoroughly dust down all surfaces. Best results can be achieved if the manually cleaned surface is primed with protectomastic- self-priming surface tolerant coating; otherwise, treatment with metal conditioning solution will also produce satisfactory results.
The surface should be clean & dry before application of primer coat.

 

Application :

  • Mix the contents thoroughly before & during use.
  • Apply with suitable thinner for the recommended dry film thickness.
  • Brush / Roller: add up to 5% thinner if required during application.
  • Conventional spray: add up to 15-20% thinner depending on conditions. Use only standard equipment at an atomizing pressure of 3.5-4.9 Kg/cm2.

 

Note :

  • Do not apply when temperature falls below 10˚ C or rises above 50˚ C & when relative humidity rises above 90%. Do not apply during rain Fog or mist.
  • Brushes & Roller should be cleaned with thinner otherwise, equipment is liable to be damaged.
  • Primed steel work should not be exposed with one coat for a long period.